Ce % Cerium base
Standard AlloyPurityComposition
Ce - Gd99.5 - 99.99 %
Ce - Sm99.5 - 99.9 %
CeF3 Cerium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)6.16
Melting Point (°C)1418
CeF3 Cerium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)6.16
Melting Point (°C)1418
Evaporation Temperature (°C)1400
ShapeGranules
CeF3 / CaF2 Cerium Fluoride / Calcium Fluoride
Purity99.9 %
Composition50 / 50
ShapeGranules / Disks
CeO2 Cerium Oxide
Purity99.9 - 99.99 %
Density (g/cm³)7.22
Melting Point (°C)2400
Cr2O3 Chromium (III) Oxide
Purity99.9 - 99.99 %
Density (g/cm³)5.21
Melting Point (°C)2435
Cr-SiO Chromium-Silicon Monooxide
Purity99.9 - 99.99 %
Cr % Chromium base
Standard AlloyPurityComposition
Cr - Si99.9 - 99.95 %
Cr - SiO99.9 %
Cr2O3 Chromium Oxide
Purity99.9 - 99.999 %
Density (g/cm³)5.20
Melting Point (°C)2453
Evaporation Temperature (°C)2000
ShapeGranules / Disks
Co % Cobalt base
Standard AlloyPurityComposition
Co - Cr99.9 %
Co - Ni99.95 %
Co - Sm99.9 - 99.99 %
Lu2SiO5:Ce Dilutetium Silicon Pentaoxide
Dimensionsmax. Ø 60 mm × 50 mm
Growth TechniqueBridgman
Orientation(0001) z-cut
DopingCe
Surface1 side / 2 sides polished
StructureTrigonal
Lattice Constanta = 1.425 nm
b = 1.024 nm
c = 0.664 nm
γ = 122 °Melting Point2047 °C
Density7.4 g/cm3
Thermal Expansion Coefficient19.5 × 10-6 K-1
Refractive Index1.82 @ 418 nm
Hardness5.8 M