CdSe Cadmium Selenide
Purity99.999 %
Density (g/cm³)5.81
Melting Point (°C)1350
Evaporation Temperature (°C)540
ShapeGranules
CdS Cadmium Sulfide
Dimensions10 mm × 10 mm × 0,5 mm
max. 25 mm × 25 mm × 15 mmGrowth TechniquePhysical Vapor Transport
Orientation(0001)
(11-20)
(10-10)Surface1 side / 2 sides polished
StructureHexagonal
Lattice Constanta = 0.414 nm
c = 0.672 nmMelting Point1287 °C
Density4.82 g/cm3
Thermal Expansion Coefficient4.6 × 10-6 K-1 @ a-Achse
2.5 × 10-6 K-1 @ c-AchseDielectric Constant8.9 @ 300 K
Thermal Conductivity2.7 W cm-1 K-1 @ 300 K
Electron Mobility250 cm2 V-1 s-1 @ 300 K
Band Gap2.42 eV
CdS Cadmium Sulfide
Purity99.9 - 99.999 %
Density (g/cm³)4.82
Melting Point (°C)1750
CdS Cadmium Selenide
Purity99.999 %
Density (g/cm³)4.82
Melting Point (°C)1750
Evaporation Temperature (°C)800
ShapeGranules
CdTe Cadmium Telluride
Dimensions10 mm × 10 mm × 0.5 mm
Growth TechniquePhysical Vapor Transport
Orientation(100)
(110)
(111)Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.648 nm
Melting Point1091 °C
Density5.85 g/cm3
Thermal Expansion Coefficient5.9 × 10-6 K-1
Dielectric Constant11.1 @ 300 K
Thermal Conductivity6.2 W cm-1 K-1 @ 300 K
Electron Mobility700 cm2 V-1 s-1 @ 300 K
Band Gap1.56 eV
CdTe Cadmium Telluride
Purity99.9 - 99.999 %
Density (g/cm³)5.85
Melting Point (°C)1121
CdTe Cadmium Telluride
Purity99.999 %
Density (g/cm³)5.85
Melting Point (°C)1121
Evaporation Temperature (°C)450
ShapeGranules
CdWO4 Cadmium Tungstate
Dimensionsmax. Ø 35 mm × 200 mm
Growth TechniqueCzochralski
Orientation(101)
Dopingundoped
Surface1 side / 2 sides polished
StructureMonoclinic
Lattice Constanta = 0.503 nm
b = 0.586 nm
c = 0.507 nm
β = 91.52 °Melting Point1325 °C
Density7.9 g/cm3
Thermal Expansion Coefficient10.2 × 10-6 K-1
Refractive Index2.2 - 2.3 @ 475 nm
Hardness4 - 4.5 M
Csl Caesium Iodide
Dimensions10 mm × 10 mm × 0.5 mm
max. Ø 100 mm × 300 mmGrowth TechniqueBridgman / Czochralski
Orientation(111)
Dopingundoped, Tl, Na
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.457 nm
Melting Point894 °C
Density4.51 g/cm3
Thermal Expansion Coefficient39.1 × 10-6 K-1
Refractive Index1.637 @ 50 μm
Hardness2 M
CaF2 Calcium Fluoride
DimensionsØ 2" - 4"
max. Ø 8" × 150 mmGrowth TechniqueBridgman
Orientation(111)
Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.546 nm
Melting Point1418 °C
Density3.18 g/cm3
Refractive Index1.308 @ 9.7 μm
Hardness4 M
CaCO3 Calcium Carbonate
Dimensions10 mm × 10 mm × 0.5 mm
Growth TechniqueGEL Growth Technique
Orientationundoped
Surface1 side / 2 sides polished
StructureTrigonal
Lattice Constanta = 0.499 nm
c = 1.708 nmMelting Point1339 °C
Density2.711 g/cm3
Thermal Expansion Coefficient24.39 × 10-6 K-1 @ a-axis
5.68 × 10-6 K-1 @ c-axisRefractive Indexn0 = 1.6654 @ 509 nm
ne = 1.4898 @ 509 nmHardness3 M
CaF2 Calcium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)3.13
Melting Point (°C)1360
CaF2 Calcium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)3.13
Melting Point (°C)1360
Evaporation Temperature (°C)1280 - 1400
ShapeGranules
CeO2 Cerium (IV) Oxide
Purity99.9 - 99.99 %
Density (g/cm³)7.30
Melting Point (°C)2600
Evaporation Temperature (°C)1950
ShapeGranules / Disks