Zr % Zirconium base
Standard AlloyPurityComposition
Zr - Fe99.9 %
Zr - Nb99.9 %
Zr - Ni99.9 %
Zr - Ti99.9 %
Zr - Y99.9 %
ZrB2 Zirconium Boride
Purity99.9 - 99.99 %
Density (g/cm³)6.09
Melting Point (°C)3040
ZrC Zirconium Carbide
Purity99.9 - 99.999 %
Density (g/cm³)6.73
Melting Point (°C)3540
Evaporation Temperature (°C)2500
ShapeGranules
ZrN Zirconium Nitride
Purity99.9 - 99.99 %
Density (g/cm³)7.09
Melting Point (°C)2980
ZrO2 Zirconium Oxide
Purity99.9 - 99.99 %
Density (g/cm³)5.68
Melting Point (°C)2715
ZrO2 Zirconium Oxide
Purity99.99 - 99.999 %
Density (g/cm³)4.90
Melting Point (°C)2700
Evaporation Temperature (°C)2200
ShapeGranules
ZrO2 / Al2O3 Zirconium Oxide / Aluminium Oxide
Purity99.9 %
Composition40 / 60
ShapeGranules / Disks
ZrO2 / Ta2O5 Zirconium Oxide / Tantal Oxide
Purity99.99 %
Composition70 / 30, 50 / 50
ShapeGranules / Disks
ZrO2 / TiO2 Zirconium Oxide / Titanium Oxide
Purity99.99 %
Composition50 / 50, 40 / 60
ShapeGranules / Disks
ZrO2 / Y2O3 Zirconium Oxide / Yttrium Oxide
Purity99.99 %
Composition80 / 20
ShapeGranules / Disks
BaB2O4 β-Barium Borate
Dimensions4 mm × 4 mm × 7 mm
8 mm × 4 mm × 7 mm
as substrates or prismGrowth TechniqueCzochralski
Orientationz axis
Dopingundoped
Surface1 side / 2 sides polished
StructureTrigonal
Lattice Constanta = b = 1.253 nm
c = 1.272 nm
Z = 7Melting Point1095 °C
Density3.85 g/cm3
Thermal Expansion Coefficient4.0 × 10-6 K-1 @ a axis
36 × 10-6 K-1 @ c axisRefractive Indexne = 1.5425 @ 1064 nm
n0 = 1.6551 @ 1064 nmHardness4.5 M