Y2Al5O12 Yttrium Aluminium Garnet (YAG)
Dimensions10 mm × 10 mm × 0.5 mm
Ø 2" × 0.5 mmGrowth TechniqueCzochralski
Orientation(100)
(110)
(111)Dopingundoped, Nd, Ce
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 1.201 nm
Melting Point1970 °C
Density4.56 g/cm3
Thermal Expansion Coefficient7.8 × 10-6 K-1 @ [111] axis
Refractive Index1.82 @ 632.8 nm
Hardness8.5 M
YAlO3 Yttrium Aluminium Oxide
Dimensions10 mm × 10 mm × 0.5 mm
max. Ø 30 mm × 50 mmGrowth TechniqueCzochralski
Orientation(100)
(110)
(111)Dopingundoped
Surface1 side / 2 sides polished
StructureOrthorhombic
Lattice Constanta = 0.518 nm
b = 0.533 nm
c = 0.737 nmMelting Point1870 °C
Density4.88 g/cm3
Thermal Expansion Coefficient2 - 10 × 10-6 K-1
Dielectric Constant16 - 20
Hardness8 M
YBCO Yttrium Barium Copper Oxide / YBa2Cu3O7
Purity99.9 - 99.99 %
Density (g/cm³)6.30
Melting Point (°C)~ 1000
YSZ Yttria-Stabilized Zirconia
Dimensions10 mm × 10 mm × 0.5 mm
Ø 2" × 0.5 mmGrowth TechniqueArc Melting
Orientation(100)
(110)
(111)Dopingundoped
Surface1 side / 2 sides polished
Composition8 bzw. 13 mol% Y2O3
StructureCubic
Lattice Constanta = 0.512 nm
Melting Point2500 °C
Density5.8 g/cm3
Thermal Expansion Coefficient10.3 × 10-6 K-1
Dielectric Constant27
Hardness~ 8 M
YSZ Yttrium-Stabilized Zirconia
Purity99.9 - 99.99 %
Density (g/cm³)5.80
Melting Point (°C)2500
YF3 Yttrium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)4.01
Melting Point (°C)1387
Evaporation Temperature (°C)1400 - 1600
ShapeGranules
Y2O3 Yttrium Oxide
Purity99.9 - 99.99 %
Density (g/cm³)5.01
Melting Point (°C)2425
Y2O3 Yttrium Oxide
Purity99.99 - 99.999 %
Density (g/cm³)4.80
Melting Point (°C)2680
Evaporation Temperature (°C)2500
ShapeGranules
YVO4 Yttrium Vanadate
Dimensions5 mm × 5 mm × 0.5 mm
max. Ø 30 mmGrowth TechniqueCzochralski
Orientation(100)
(110)
(111)Dopingundoped. Nb
Surface1 side / 2 sides polished
StructureTetragonal
Lattice Constanta = 0.712 nm
c = 0.629 nmMelting Point1825 °C
Density4.22 g/cm3
Thermal Expansion Coefficient4.33 × 10-6 K-1 @ a axis
11.37 × 10-6 K-1 @ c axisRefractive Index1.95 @ 1340 nm
Hardness4 - 5 M
Zn % Zinc base
Standard AlloyPurityComposition
Zn - Al99.9 - 99.999 %
Zn - Mg99.9 %
Zn - Sn99.9 - 99.999 %
ZnO Zinc Oxide
Dimensions10 mm × 10 mm × 0.5 mm
max. 20 mm × 20 mm × 10 mmGrowth TechniqueHydrothermal
Orientation(0001)
Dopingundoped. Ga
Surface1 side / 2 sides polished
StructureHexagonal
Lattice Constanta = 0.332 nm
c = 0.521 nmMelting Point1975 °C
Density5.60 g/cm3
Thermal Expansion Coefficient2.9 × 10-6 K-1
Refractive Indexn0 = 1.89 @ 4 μm
ne = 1.91 @ 4 μmHardness4 M
ZnO Zinc Oxide
Purity99.9 - 99.999 %
Density (g/cm³)5.61
Melting Point (°C)1975
ZnO Zinc Oxide
Purity99.99 - 99.999 %
Density (g/cm³)5.60
Melting Point (°C)1975
Evaporation Temperature (°C)1800
ShapeGranules / Disks