BaF2 Barium Fluoride
Dimensionsmax. Ø 2” × 80 mm
Growth TechniqueBridgman
Orientation(111)
Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.620 nm
Melting Point1368 °C
Density4.893 g/cm3
Thermal Expansion Coefficient16.5 × 10-6 K-1
Refractive Index1.397 @ 10.3 μm
Hardness3 M
BaF2 Barium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)4.80
Melting Point (°C)1280
BaF2 Barium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)4.80
Melting Point (°C)1280
Evaporation Temperature (°C)1300 - 1500
ShapeGranules
BaO Barium Oxide
Purity99.99 - 99.999 %
Density (g/cm³)5.72
Melting Point (°C)1918
Evaporation Temperature (°C)1300
ShapeGranules
BaTiO3 Barium Titanate
Dimensions5 mm × 5 mm × 0.5 mm
10 mm × 10 mm × 0.5 mmGrowth TechniqueTop Seeded Solution Growth
Orientation(100)
(110)
(111)Dopingundoped
Surface1 side / 2 sides polished
StructureTetragonal (9 °C < T < 130,5 °C)
Perovskite TypeLattice Constanta = 0.399 nm
c = 0.404 nmMelting Point1600 °C
Density6.02 g/cm3
Dielectric Constantεa = 3700, εc = 135 (frei)
εa = 2400, εc = 60 (geklemmt)Refractive Indexn0 = 2.416 @ 632.8 nm
ne = 2.363 @ 632.8 nmHardness5 M
BaTiO3 Barium Titanate
Purity99.9 - 99.99 %
Density (g/cm³)6.02
Melting Point (°C)1625
BaTiO3 Barium Titanate
Purity99.9 - 99.99 %
Density (g/cm³)6.00
Melting Point (°C)1620
ShapeGranules
BaZrO3 Barium Zirconate
Purity99.9 - 99.99 %
Density (g/cm³)5.52
Melting Point (°C)2500
Bi4Ge3O12 Bismuth Germanate (BGO12)
DimensionsØ 2" (max. Ø 4")
as substrates or prismGrowth TechniqueCzochralski
Orientation(100)
Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 1.052 nm
Melting Point1045 °C
Density7.13 g/cm3
Thermal Expansion Coefficient7.0 × 10-6 K-1
Dielectric Constantε11 = 40
Refractive Index2.05602 @ 1 μm
Hardness5 M
Bi12GeO20 Bismuth Germanate (BGO20)
Dimensions10 mm × 10 mm × 0.5 mm
as substrates or prismGrowth TechniqueCzochralski
Orientation(100)
(110)Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 1.015 nm
Melting Point930 °C
Density9.20 g/cm3
Dielectric Constantε11 = 40
Refractive Index2.45 @ 632.8 nm
Hardness4.5 M
Bi2O3 Bismuth Oxide
Purity99.9 - 99.99 %
Density (g/cm³)8.55
Melting Point (°C)860
Bi2O3 Bismuth Oxide
Purity99.9 - 99.99 %
Density (g/cm³)8.90
Melting Point (°C)820
Evaporation Temperature (°C)1400
ShapeGranules / Disks
Bi12SiO20 Bismuth Silicate (BSO)
Dimensions5 mm × 5 mm × 0.5 mm
Growth TechniqueCzochralski
Orientation(100)
(110)Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 1.015 nm
Melting Point900 °C
Density9.2 g/cm3
Dielectric Constant56
Refractive Index2.54 @ 632.,8 nm
Hardness4.5 M