MgO Magnesium Oxide
Purity99.9 - 99.999 %
Density (g/cm³)3.58
Melting Point (°C)2800
Evaporation Temperature (°C)2000
ShapeGranules / Disks
MnO Manganese (IV) Oxide
Purity99.9 - 99.99 %
Density (g/cm³)5.02
Melting Point (°C)535
ShapeGranules
Mo % Molybdenum base
Standard AlloyPurityComposition
Mo - Nb99.95 %
Mo - Si99.9 %
MoO3 Molybdenum Oxide
Purity99.9 %
Density (g/cm³)4.69
Melting Point (°C)795
MoSi2 Molybdenum Silicide
Purity99.9 - 99.99 %
Density (g/cm³)6.26
Melting Point (°C)2030
NaCl Sodium Chloride
Dimensions10 mm × 10 mm × 1 mm
max. Ø 120 mm × 100 mmGrowth TechniqueKyropoulos
Orientation(100)
(110)Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.564 nm
Melting Point801 °C
Density2.17 g/cm3
Thermal Expansion Coefficient36.4 × 10-6 K-1
Refractive Index1.091 @ 30 μm
Hardness3 M
NaF Sodium Fluoride
Purity99.9 - 99.99 %
Density (g/cm³)2.79
Melting Point (°C)988
Evaporation Temperature (°C)1200
ShapeGranules
Nal Sodium Iodide
Dimensions10 mm × 10 mm × 1 mm
max. Ø 100 mm × 300 mmGrowth TechniqueBridgman
Orientation(100)
(110)Dopingundoped
Surface1 side / 2 sides polished
StructureCubic
Lattice Constanta = 0.646 nm
Melting Point661 °C
Density3.67 g/cm3
Thermal Expansion Coefficient47.7 × 10-6 K-1
Refractive Index1.356 @ 40 μm
Hardness2 M
NdCaAlO4 Neodymium Calcium Aluminate
Dimensions10 mm × 10 mm × 0.5 mm
Growth TechniqueCzochralski
Orientation(100)
Dopingundoped
Surface1 side / 2 sides polished
StructureTetragonal
Lattice Constanta = 0.369 nm
c = 1.212 nmMelting Point1850 °C
Density5.56 g/cm3
Thermal Expansion Coefficient12 × 10-6 K-1
Dielectric Constant19.5
NdGaO3 Neodymium Gallium Oxide
Dimensions10 mm × 10 mm × 0.5 mm
Ø 2" × 0.5 mmGrowth TechniqueCzochralski
Orientation(100)
(110)
(111)Dopingundoped
Surface1 side / 2 sides polished
StructureOrthorhombic
Lattice Constanta = 0.543 nm
b = 0.550 nm
c = 0.771 nmMelting Point1600 °C
Density7.57 g/cm3
Thermal Expansion Coefficient7.8 × 10-6 K-1
Dielectric Constant25
Hardness5.9 M