Growth TechniqueLiquid Encapsulated Czochralski / Bridgman
Orientation(100)
(110)
(111)
StructureCubic (Zincblende)
Lattice Constanta = 0.648 nm
Thermal Expansion Coefficient5.37 × 10-6K-1
Dielectric Constant16.8 @ 300 K
Thermal Conductivity0.18 W cm-1K-1
Electron Mobility7.7×104cm2 V-1s-1@ 300 K